Product line-up

Our extensive product line-up includes cermet. Not all products are shown, so please contact us for more details.

WC

WC/12%Co

Composition
/manufacturing
Product name Particle size Characteristics
WC/12%Co
Agglomerated and sintered method
SURPREX WC12L -53+15µm High hardness
Wear resistance
Abrasion resistance
SURPREX WC12J -45+15µm
SURPREX WC12D -38+10µm
DTS-W171-75/32 -75+32µm
DTS-W76-30/5 -30+5µm
DTS-W160-45/15 -45+15µm WC primary particle size (large)
Wear resistance
DTS-W232-53/15 -53+15µm WC primary particle size (large)
Wear resistance
DTS-W522-45/15 -45+15µm Low carbon content
Solvent resistance (molten metal)

WC/17%Co

Composition
/manufacturing
Product name Particle size Characteristics
WC/17%Co
Agglomerated and sintered method
SURPREX WC17L -53+15µm High toughness
Wear resistance
SURPREX WC17J -45+15µm
SURPREX WC17D -38+10µm
DTS-W398-10/0 -10+0µm

WC/20%CrC/7%Ni

Composition
/manufacturing
Product name Particle size Characteristics
WC/20%CrC/7%Ni
Agglomerated and sintered method
SURPREX W2007L -53+15µm Wear resistance
Corrosion resistance
Resistance to slurry erosion
Oxidation resistance
SURPREX W2007J -45+15µm
SURPREX W2007D -38+10µm
DTS-W74-30/5 -30+5µm
DTS-W374-10/0 -10+0µm
DTS-W94-45/15 -45+15µm WC primary particle size (large)
Wear resistance

WC/10%Co/4%Cr

Composition
/manufacturing
Product name Particle size Characteristics
WC/10%Co/4%Cr
Agglomerated and sintered method
SURPREX W1004J -45+15µm High hardness
High toughness
Wear resitance
Corrosion resistance
Resistance to slurry erosion
DTS-W375-53/15 -53+15µm
DTS-W172-38/10 -38+10µm
DTS-W108-30/5 -30+5µm
DTS-W297-10/0 -10+0µm
DTS-W360-45/15 -45+15µm WC primary particle size (large)
Resistance to slurry erosion
Resistance to cavitation erosion

WC/10%Ni

Composition
/manufacturing
Product name Particle size Characteristics
WC/10%Ni
Agglomerated and sintered method
DTS-W141-45/15 -45+15µm Wear resistance
Corrosion resistance

WC/Hastelloy

Composition
/manufacturing
Product name Particle size Characteristics
WC/12% Hastelloy
Agglomerated and sintered method
DTS-W124-45/15 -45+15µm Wear resistance
Corrosion resistance
WC/30% Hastelloy
Agglomerated and sintered method
DTS-W296-53/20 -53+20µm Wear resistance
Corrosion resistance

WC/NiCr

Composition
/manufacturing
Product name Particle size Characteristics
WC/20%NiCr
Agglomerated and sintered method
DTS-W291-53/20 -53+20µm Wear resistance
Corrosion resistance

Impact resistant cermet

Composition
/manufacturing
Product name Particle size Characteristics
WC/CrNi
Agglomerated and sintered method
SURPREX W2010XJ -45+15µm High adhesive strength
Shock resistance
Wear resistance
Resistance to slurry erosion
SURPREX W2010XS -38+10µm
WC/NiCr
Agglomerated and sintered method
SURPREX W2011XJ -45+15µm
SURPREX W2011XS -38+10µm
WC/NiCr
Agglomerated and sintered method
SURPREX W2021XJ -45+15µm Shock resistance (the best in the shock resistance series)
Wear resistance
SURPREX W2021XS -38+10µm

WC/Fe

WC/Fe based allowy - for low temperature thermal spray processes

Composition
/manufacturing
Product name Particle size Characteristics
WC/Fe based alloy
Agglomerated and sintered method
Please contact Fujimi for details -45+15µm
-20+5µm
Wear resistance
Corossion resistance
Low surface roughness

Aerospace materials

Aerospace materials

Composition
/manufacturing
Product name Particle size Characteristics
WC/17%Co
Agglomerated and sintered method
AMS7881A
compliant
-45+20µm High toughness
Wear resistance
AMS7881A
compliant
-53+15µm
WC/10%Co/4%Cr
Agglomerated and sintered method
AMS7882A
compliant
-53+15µm High hardness
High toughness
Wear resistance
Corrosion resistance

CrC

CrC/NiCr

Composition
/manufacturing
Product name Particle size Characteristics
CrC/20%NiCr
Agglomerated and sintered method
SURPREX CNC20J(4) -45+15µm Wear resistance at high temperatures
SURPREX CNC20J(6)
SURPREX CNC20J(8)
CrC/25%NiCr
Agglomerated and sintered method
SURPREX CNC25J(4) -45+15µm Wear resistance for high temperatures
Oxidation resistance
SURPREX CNC25J(6)
SURPREX CNC25J(8)
DTS-C105-53/10 -53+10µm
DTS-C60-38/10 -38+10µm
DTS-C68-30/5 -30+5µm
CrC/30%NiCr
Agglomerated and sintered method
DTS-C106-53/15 -53+15µm
CrC/35%NiCr
Agglomerated and sintered method
DTS-C164-53/15 -53+15µm
DTS-C112-38/10 -38+10µm

MoB

MoB/CoCr

Composition
/manufacturing
Product name Particle size Characteristics
MoB/CoCr
Agglomerated and sintered method
DTS-B26-53/15 -53+15µm Durability against molten metal/alloys
DTS-B49-45/15 -45+15µm
DTS-B46-38/10 -38+10µm
DTS-B47-30/5 -30+5µm

MoB/NiCr

Composition
/manufacturing
Product name Particle size Characteristics
MoB/NiCr
Agglomerated and sintered method
DTS-B14-53/15 -53+15µm Durability against molten metal/alloys
DTS-B57-30/5 -30+5µm

Al2O3

Al2O3 (White alumina)

Composition
/manufacturing
Product name Particle size Characteristics
Al2O3 99.6% up
Molten grinding method
SURPREX AW24 -75+38µm White
Wear resistance
Insulation properties
Chemical stability
Resistance to plasma erosion
SURPREX AW28 -63+32µm
SURPREX AW32 -53+25µm
SURPREX AW36 -53+20µm
SURPREX AW40 -53+15µm
SURPREX AW50 -45+10µm
SURPREX AW60 -38+8µm
SURPREX AW120 -25+5µm
Al2O3 99.6% up
Molten grinding method
*Liquidity improvement product
SURPREX AW36R -53+20µm
SURPREX AW50R -45+10µm
SURPREX AW60R -38+8µm
SURPREX AW120R -25+5µm

Al2O3-3%TiO2 (Gray alumina)

Composition
/manufacturing
Product name Particle size Characteristics
Al2O3-3%TiO2
Molten grinding method
SURPREX AG24 -75+38µm High toughness
Wear resistance
Heat resistance
Shock resistance
SURPREX AG28 -63+32µm
SURPREX AG32 -53+25µm
SURPREX AG36 -53+20µm
SURPREX AG40 -53+15µm
SURPREX AG50 -45+10µm
SURPREX AG60 -38+8µm
SURPREX AG120 -25+5µm
Al2O3-3%TiO2
Molten grinding method
*Liquidity improvement product
SURPREX AG36R -53+20µm
SURPREX AG50R -45+10µm
SURPREX AG60R -38+8µm
SURPREX AG120R -25+5µm

High purity alumina

Composition
/manufacturing
Product name Particle size Characteristics
Al2O3 99.9% up
Molten grinding method
SURPREX AHP50 -45+10µm Low color spot density
Wear resistance
Insulation properties
Chemical stability
Resistance to plasma erosion
SURPREX AHP60 -38+8µm
Al2O3 99.99% up
Agglomerated and sintered method
DTS-A97-45/10 -45+10µm

Alumina-titania

Composition
/manufacturing
Product name Particle size Characteristics
Al2O3-13%TiO2
Agglomerated and sintered method
DTS-AT21-63/10 -63+10µm Wear resistance
Wear and slip resistance
Specularity
Al2O3-40%TiO2
Agglomerated and sintered method
DTS-AT32-63/15 -63+15µm

Spinel

Composition
/manufacturing
Product name Particle size Characteristics
Al2O3-MgO
Molten griding method
SURPREX Q2 -45+10µm Wear resistance
Corrosion resistance

Mullite

Composition
/manufacturing
Product name Particle size Characteristics
Al2O3-SiO2
Molten grinding method
DTS-A53-45/10 -45+10µm Heat insulation
Thermal shock resistance
Chemical stability

Y2O3

High purity yttria

Composition
/manufacturing
Product name Particle size Characteristics
Y2O3 99.9% up
Agglomerated and sintered method
SURPREX Y12 -63+10µm Heat resistance
Corrosion resistance
Chemical stability
Resistance to plasma erosion
DTS-Y27-63/10

ZrO2

Zirconia

Composition
/manufacturing
Product name Particle size Characteristics
ZrO2 99.0% up
Molten grinding method
DTS-Z100-45/10 -45+10µm Heat resistance
Heat insulation

Stabilized zirconia

Composition
/manufacturing
Product name Particle size Characteristics
ZrO2 - 8%Y2O3
Agglomerated and sintered method
DTS-Z121-63/10 -63+10µm High electrical conductivity
Oxygen ion conductivity
Heat resistance
Heat insulation
High hardness
Chemical stability
ZrO2 - 8%Y2O3
Molten grinding method
SURPREX Z10 -45+10µm

Zircon

Composition
/manufacturing
Product name Particle size Characteristics
ZrO2-SiO2
Molten grinding method
DTS-J8-45/10 -45+10µm Heat insulation
Thermal shock resistance
Chemical stability

MgO

Cordierite

Composition
/manufacturing
Product name Particle size Characteristics
MgO-2Al2O3-5SiO2
Agglomerated and sintered method
DTS-A76-63/10 -63+10µm Heat insulation
Thermal shock resistance

YAG

YAG

Composition
/manufacturing
Product name Particle size Characteristics
YAG
Agglomerated and sintered process
DTS-YA7-75/20 -75+20µm Heat resistance
Chemical stability

Page Top