Our extensive product line-up includes cermet. Not all products are shown, so please contact us for more details.

WC

Thermal Spray Materials catalogue files

WC/12%Co

Composition /manufacturing	Product name	Particle size	Characteristics
WC/12%Co Agglomerated and sintered method	SURPREX WC12L	-53+15µm	High hardness Wear resistance Abrasion resistance
	SURPREX WC12J	-45+15µm
	SURPREX WC12D	-38+10µm
	DTS-W171-75/32	-75+32µm
	DTS-W76-30/5	-30+5µm
	DTS-W522-45/15	-45+15µm	Low carbon content Solvent resistance (molten metal)

WC/17%Co

Composition /manufacturing	Product name	Particle size	Characteristics
WC/17%Co Agglomerated and sintered method	SURPREX WC17L	-53+15µm	High toughness Wear resistance
	SURPREX WC17J	-45+15µm
	SURPREX WC17D	-38+10µm

WC/20%CrC/7%Ni

Composition /manufacturing	Product name	Particle size	Characteristics
WC/20%CrC/7%Ni Agglomerated and sintered method	SURPREX W2007L	-53+15µm	Wear resistance Corrosion resistance Resistance to slurry erosion Oxidation resistance
	SURPREX W2007J	-45+15µm
	SURPREX W2007D	-38+10µm
	DTS-W74-30/5	-30+5µm

WC/10%Co/4%Cr

Composition /manufacturing	Product name	Particle size	Characteristics
WC/10%Co/4%Cr Agglomerated and sintered method	SURPREX W1004J	-45+15µm	High hardness High toughness Wear resitance Corrosion resistance Resistance to slurry erosion
	DTS-W375-53/15	-53+15µm
	DTS-W172-38/10	-38+10µm
	DTS-W108-30/5	-30+5µm
	DTS-W360-45/15	-45+15µm	WC primary particle size (large) Resistance to slurry erosion Resistance to cavitation erosion

WC/10%Ni

Composition /manufacturing	Product name	Particle size	Characteristics
WC/10%Ni Agglomerated and sintered method	DTS-W141-45/15	-45+15µm	Wear resistance Corrosion resistance

WC/Hastelloy

Composition /manufacturing	Product name	Particle size	Characteristics
WC/12% Hastelloy Agglomerated and sintered method	DTS-W124-45/15	-45+15µm	Wear resistance Corrosion resistance
WC/30% Hastelloy Agglomerated and sintered method	DTS-W296-53/20	-53+20µm	Wear resistance Corrosion resistance

Impact resistant cermet

Composition /manufacturing	Product name	Particle size	Characteristics
WC/CrNi Agglomerated and sintered method	SURPREX W2010XJ	-45+15µm	High adhesive strength Shock resistance Wear resistance Resistance to slurry erosion
WC/NiCr Agglomerated and sintered method	SURPREX W2011XJ	-45+15µm
WC/NiCr Agglomerated and sintered method	SURPREX W2021XJ	-45+15µm	Shock resistance (the best in the shock resistance series) Wear resistance

WC/Fe

Thermal Spray Materials catalogue files

WC/Fe based allowy - for low temperature thermal spray processes

Composition /manufacturing	Product name	Particle size	Characteristics
WC/Fe based alloy Agglomerated and sintered method	Please contact Fujimi for details	-45+15µm -20+5µm	Wear resistance Corossion resistance Low surface roughness

Aerospace materials

Thermal Spray Materials catalogue files

Aerospace materials

Composition /manufacturing	Product name	Particle size	Characteristics
WC/17%Co Agglomerated and sintered method	AMS7881A compliant	-45+20µm	High toughness Wear resistance
WC/17%Co Agglomerated and sintered method	AMS7881A compliant	-53+15µm	High toughness Wear resistance
WC/10%Co/4%Cr Agglomerated and sintered method	AMS7882A compliant	-53+15µm	High hardness High toughness Wear resistance Corrosion resistance

CrC

Thermal Spray Materials catalogue files

CrC/NiCr

Composition /manufacturing	Product name	Particle size	Characteristics
CrC/20%NiCr Agglomerated and sintered method	SURPREX CNC20J(4)	-45+15µm	Wear resistance at high temperatures
	SURPREX CNC20J(6)
	SURPREX CNC20J(8)
CrC/25%NiCr Agglomerated and sintered method	SURPREX CNC25J(4)	-45+15µm	Wear resistance for high temperatures Oxidation resistance
	SURPREX CNC25J(6)
	SURPREX CNC25J(8)
	DTS-C105-53/10	-53+10µm
	DTS-C60-38/10	-38+10µm

MoB

Thermal Spray Materials catalogue files

MoB/CoCr

Composition /manufacturing	Product name	Particle size	Characteristics
MoB/CoCr Agglomerated and sintered method	DTS-B49-45/15	-45+15µm	Durability against molten metal/alloys
MoB/CoCr Agglomerated and sintered method	DTS-B47-30/5	-30+5µm	Durability against molten metal/alloys

Al₂O₃

Thermal Spray Materials catalogue files

Al₂O₃ (White alumina)

Composition /manufacturing	Product name	Particle size	Characteristics
Al₂O₃ 99.6% up Molten grinding method *Liquidity improvement product	SURPREX AW36R	-53+20µm	White Wear resistance Insulation properties Chemical stability Resistance to plasma erosion
	SURPREX AW50R	-45+10µm
	SURPREX AW60R	-38+8µm

Al₂O₃-3%TiO₂ (Gray alumina)

Composition /manufacturing	Product name	Particle size	Characteristics
Al₂O₃-3%TiO₂ Molten grinding method *Liquidity improvement product	SURPREX AG36R	-53+20µm	High toughness Wear resistance Heat resistance Shock resistance
	SURPREX AG50R	-45+10µm

High purity alumina

Composition /manufacturing	Product name	Particle size	Characteristics
Al₂O₃ 99.9% up Molten grinding method	SURPREX AHP50	-45+10µm	Low color spot density Wear resistance Insulation properties Chemical stability Resistance to plasma erosion
Al₂O₃ 99.9% up Molten grinding method	SURPREX AHP60	-38+8µm

Spinel

Composition /manufacturing	Product name	Particle size	Characteristics
Al₂O₃-MgO Agglomerated and sintered method	DTS-Q35-53/10	-53+10µm	Wear resistance Corrosion resistance

Mullite

Composition /manufacturing	Product name	Particle size	Characteristics
Al₂O₃-SiO₂ Molten grinding method	DTS-A53-45/10	-45+10µm	Heat insulation Thermal shock resistance Chemical stability

Y₂O₃

Thermal Spray Materials catalogue files

High purity yttria

Composition /manufacturing	Product name	Particle size	Characteristics
Y₂O₃ 99.9% up Agglomerated and sintered method	SURPREX Y12	-63+10µm	Heat resistance Corrosion resistance Chemical stability Resistance to plasma erosion
Y₂O₃ 99.9% up Agglomerated and sintered method	DTS-Y110-63/10	-63+10µm

ZrO₂

Thermal Spray Materials catalogue files

Stabilized zirconia

Composition /manufacturing	Product name	Particle size	Characteristics
ZrO₂ - 8%Y₂O₃ Agglomerated and sintered method	DTS-Z121-63/10	-63+10µm	High electrical conductivity Oxygen ion conductivity Heat resistance Heat insulation High hardness Chemical stability
ZrO₂ - 8%Y₂O₃ Molten grinding method	SURPREX Z10	-45+10µm

Zircon

Composition /manufacturing	Product name	Particle size	Characteristics
ZrO₂-SiO₂ Molten grinding method	DTS-J8-45/10	-45+10µm	Heat insulation Thermal shock resistance Chemical stability

MgO

Thermal Spray Materials catalogue files

Cordierite

Composition /manufacturing	Product name	Particle size	Characteristics
MgO-2Al₂O₃-5SiO₂ Agglomerated and sintered method	DTS-A76-63/10	-63+10µm	Heat insulation Thermal shock resistance

YAG

Thermal Spray Materials catalogue files

YAG

Composition /manufacturing	Product name	Particle size	Characteristics
YAG Agglomerated and sintered process	DTS-YA7-75/20	-75+20µm	Heat resistance Chemical stability